An important property of alloy 601 is its resistance to oxidation at temperatures up to 1180℃. It can be used even under severe conditions. Even under severe conditions, such as heating and cooling cycles, 601 can generate a dense oxide film and obtain high resistance to flaking.

Nickel Alloy 625 is a face centered cubic crystal structure. After holding at 650 ℃ for a long enough time, carbon particles and unstable quaternary phase will be precipitated and transformed into stable Ni3 (Nb, Ti) orthorhombic lattice phase. After solution strengthening, the mechanical properties

UNS N06600 is corrosion resistant to a wide range of corrosive media. The chromium composition gives the alloy better corrosion resistance under oxidizing conditions than nickel 99.2 (alloy 200) and nickel 99.2 (alloy 201, low carbon).